一、物化性能
組成 特殊聚丙烯酸等
外觀(guān) 微黃色透明弱粘液體
離子性 弱陽(yáng)離子
溶解度 溶解于水
PH值 5～6
二、使用方法
用量：因被處理物的種類(lèi)而異，一般為6.0~10.0%（o.w.f.）
1、浸軋法
用量： HOLPOSON® HOT 80~130g/l
處理方法：二浸二軋，帶液率在80%左右，120℃以上烘干定型
2、浸漬法（適用棉、粘膠）
用量：6-10%（o.w.f.）
均勻化料整理液 浸漬（20分鐘） 脫水（帶液量50%左右） 烘干（80℃） 定型（120度，1-2分鐘）
3、熔絲法
根據(jù)實(shí)際，結(jié)合技術(shù)建議用量配制材料
注意事項(xiàng)
產(chǎn)品使用前請(qǐng)確認(rèn)面料是否處理疏水柔軟劑,建議添加親水性柔軟劑，配制好的工作液請(qǐng)于當(dāng)日內(nèi)使用
貯 存
室內(nèi)存放，避免高溫、嚴(yán)寒。
溫馨提示：本網(wǎng)站所展示單價(jià)均為200g 小樣運(yùn)費(fèi)，各產(chǎn)品實(shí)際單價(jià)待確認(rèn)要求后報(bào)價(jià)。
Hydroscopic and Heat Releasing Finishing Agent HOLPOSON® HOT
HOT is suitable for finishing cotton, viscose, polyester, acrylic and other fibers. Its working principle is as follows: The product treated on the fabric make the water vapor or sweat vapor around the fabric condense into water drops. And the condensation heat produced makes the human body feel warm, so as to achieve the function of heat storage and warmth preservation.
Physical & chemical properties:
*position: Special polyacrylic acid, etc.
Appearance: Yellowish transparent weak viscous liquid
Ionicity: Weak cationic
Solubility: Soluble in water
pH: 5-6
Usage:
Dosage: Depends on different types of materials to be treated. Generally 6.0-10.0% (o.w.f.)
1. Padding method
Dosage: HOT 80-130g/L
Treatment method: Dip and roll twice, with liquid rate of about 80%, drying and heat setting above 120 ℃
2. Impregnation method (applicable to cotton and viscose)
Dosage: 6-10% (o.w.f.)
Dissolv evenly to prepare the solution → impregnation (20 minutes) → dehydration (about 50% of liquid content) → drying (80 ℃) → heat setting (120 ℃, 1-2 minutes)
3. Melt spinning method
Prepare the solution according to the actual situation and technical suggestions.
Attentions:
Before using the product, please confirm whether the fabric is treated with hydrophobic softener. It is re*mended to add hydrophilic softener. The prepared working solution should be used within the same day.
Storage:
1. Store indoor
2. Avoid overheat and severe cold
alice